SAE 1008 Round Bars are low-carbon steel bars valued for their excellent ductility, formability, weldability and ease of fabrication. With a controlled carbon level and relatively low alloy content, this grade is suitable for a wide range of general engineering and manufacturing requirements where high strength is not the primary design objective. Jineshwar Steels supplies SAE 1008 Round Bars for customers requiring dependable material quality, consistent dimensions and commercially practical supply options. SAE J403 identifies SAE 1008 as a non-resulfurized carbon steel grade with carbon up to 0.10% and manganese up to 0.50%.

As a SAE 1008 Round Bars manufacturer, Jineshwar Steels focuses on sourcing and supplying material according to the dimensional, surface and documentation requirements specified by customers. The bars can be considered for machining components, formed parts, fabricated assemblies, pins, shafts, brackets and other applications where a low-carbon steel with good workability is appropriate. Depending on the required size and finish, customers can request suitable hot-finished, cold-finished, bright or machined forms. Availability of a particular manufacturing route, size and finish should always be confirmed against the project specification.

Table of Contents

01

SAE 1008 Round Bars Specifications

02

SAE 1008 Round Bars Chemical Composition

03

SAE 1008 Round Bars Mechanical Properties

04

SAE 1008 Round Bars Applications

05

SAE 1008 Round Bars Latest Price List

As an experienced exporter of industrial steel products, Jineshwar Steels supports domestic as well as international procurement requirements. Export orders can be prepared according to agreed dimensions, quantities, packing instructions, inspection requirements and documentation. For international buyers, proper identification of grade, size, heat or batch information and material test documentation can make incoming inspection and traceability easier. The company can coordinate with customers regarding commercial requirements before dispatch so that the supplied material matches the purchase order as closely as possible.

SAE 1008 is particularly useful when the application requires steel that can be readily formed, bent, welded or processed. Its low-carbon chemistry makes it a practical choice for components where excessive hardness is not required. However, buyers should distinguish SAE 1008 from higher-carbon grades such as SAE 1010 or SAE 1018 when strength, hardness or wear resistance is a major requirement. Material selection should therefore be based on the actual mechanical and manufacturing requirements of the finished component rather than grade name alone.

Jineshwar Steels operates as a trusted supplier for customers seeking SAE 1008 Round Bars in different diameters and supply conditions. Depending on stock and production availability, buyers can enquire for standard commercial lengths, cut lengths and customized dimensional requirements. Surface condition can also be discussed according to whether the bars will undergo machining, forming, welding or further fabrication.

For procurement teams, consistency is often as important as the nominal grade. A dependable supplier should be able to provide clear product identification, dimensional information and relevant test documentation where requested. Jineshwar Steels approaches SAE 1008 supply with an emphasis on specification matching, inspection coordination and practical delivery planning. Buyers looking to buy SAE 1008 Round Bars can provide the required diameter, length, quantity, surface finish, standard and destination so that the appropriate commercial offer can be prepared.

Parameter	Specification
Product	SAE 1008 Round Bars
Grade	SAE 1008
Material Type	Low Carbon Steel
Standard	SAE J403
UNS	G10080
Form	Round Bar
Diameter	As per customer requirement
Length	Standard / Cut Length as required
Surface	Hot Finished / Cold Finished / Bright / Machined, subject to requirement
Supply Condition	As agreed in purchase specification
Inspection	Dimensional and material testing as required
Documentation	Material Test Certificate available as applicable

Grade	C	Mn	P	S	Fe
SAE 1008	≤ 0.10%	≤ 0.50%	≤ 0.030%	≤ 0.035%	Balance

Grade	Tensile Strength (MPa)	Yield Strength (MPa)	Elongation (%)	Hardness (HB)
SAE 1008	270–410	Approx. 180–280	Approx. 28–40	Approx. 80–120